直径A Diameter	原棒尺寸 Fullsize Round Bar	直径尺寸公差 Tolerance for Diameter	调质Hardening And Tempering	制造方法 Method of Manufacturing	每米重量 Weight Per Meter(KG)
10	2000	±0.30	—	由线材冷拔而成Combined	0.623
12	2000	±0.30	—	由线材冷拔而成Combined	0.897
15	2000	±0.30	—	由线材冷拔而成Combined	1.402
20	2000	0~+0.15	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	2.492
22	2000	0~+0.15	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	3.015
25	2000	0~+0.15	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	3.893
30	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	5.606
32	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	6.378
35	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	7.630
40	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	9.966
45	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	12.62
50	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	15.58
55	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	18.85
60	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	22.43
65	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	26.32
70	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	30.52
75	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	35.04
80	2000	0~+0.25	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	39.87
85	2000	0~+0.50	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	45.00
90	2000	0~+0.50	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	50.45
95	2000	0~+0.50	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	56.21
100	2000	0~+0.50	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	62.29
120	2000	0~+0.50	—	热轧后去渣皮Removing Slag Skull after Hot Rolling	89.69

数据（参考值）Data

特性 Mechanical Properties
抗拉强度Tensile Strength	屈服强度Resistance	延伸Elongation	布氏硬度 Brinell Hardness	比重Specific Density	热传导度Thermal  Conduction Degree	纤细膨胀系数 SLinear Expansion Coefficient
520以上Over	205以上Over	40以上Over	187以下Below	7.93	16.3	17.3

化学成分（%）Chemical Composition（%）
C	Si	Mn	P	S	Ni	Cr	Mo	Cu	Fe	其他Miscellaneous
0.08以下Below	1以下Below	2以下Below	0.045以下Below	0.03以下Below	8~10.5	18~20	—	—	剩余Residual	—

概述 Summarization
不锈钢是以Steel Special Use Stainless的略写SUS为几号来表示的。在不锈钢里生产最多的种类是以SUS304为代表的奥氏体系列。
Stainless steel is indicated with the abbreviation of “Steel special Use Stainless”—SUS.Austenite series represented by SUS304are the ones that have been produced in the largest quantity among the stainless steel.
进货商品（尺寸）信息Information for Purchase of Goods（Size）
以下尺寸也能从日本进货 The goods in the following sizes may also be purchased from Japan.